1. Identificação | |
Tipo de Referência | Artigo em Revista Científica (Journal Article) |
Site | mtc-m21c.sid.inpe.br |
Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
Identificador | 8JMKD3MGP3W34R/3TC3FL2 |
Repositório | sid.inpe.br/mtc-m21c/2019/05.24.18.27 (acesso restrito) |
Última Atualização | 2019:05.24.18.27.26 (UTC) simone |
Repositório de Metadados | sid.inpe.br/mtc-m21c/2019/05.24.18.27.26 |
Última Atualização dos Metadados | 2020:01.06.11.42.14 (UTC) administrator |
DOI | 10.1016/j.jmrt.2017.12.004 |
ISSN | 2238-7854 |
Chave de Citação | DalibonPecCabTraBrü:2019:FrWeRe |
Título | Fretting wear resistance of DLC hard coatings deposited on nitrided martensitic stainless steel |
Ano | 2019 |
Mês | jan./mar. |
Data de Acesso | 21 maio 2024 |
Tipo de Trabalho | journal article |
Tipo Secundário | PRE PI |
Número de Arquivos | 1 |
Tamanho | 2723 KiB |
|
2. Contextualização | |
Autor | 1 Dalibon, Eugenia L. 2 Pecina, Jorge N. 3 Cabo, Amado 4 Trava-Airoldi, Vladimir Jesus 5 Brühl, Sônia P. |
Grupo | 1 2 3 4 LABAS-COCTE-INPE-MCTIC-GOV-BR |
Afiliação | 1 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) 2 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) 3 IONAR 4 Instituto Nacional de Pesquisas Espaciais (INPE) 5 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) |
Endereço de e-Mail do Autor | 1 2 3 4 vladimir.airoldi@inpe.br |
Revista | Journal of Materials Research and Technology |
Volume | 18 |
Número | 1 |
Páginas | 259-266 |
Histórico (UTC) | 2019-05-24 18:28:08 :: simone -> administrator :: 2019 2020-01-06 11:42:14 :: administrator -> simone :: 2019 |
|
3. Conteúdo e estrutura | |
É a matriz ou uma cópia? | é a matriz |
Estágio do Conteúdo | concluido |
Transferível | 1 |
Tipo do Conteúdo | External Contribution |
Tipo de Versão | publisher |
Palavras-Chave | DLC hard coatings Fretting wear Adhesion |
Resumo | In this work, the fretting wear behavior and adhesion of DLC coatings deposited by PACVD on nitrided and non-nitrided martensitic stainless steels were studied. Fretting wear tests were carried out with different duration and loads and pin-on-disk was also performed. The adhesion was evaluated by Rockwell C indentation and scratch test with constant and variable loads. The coating thickness was 2.5 mu m and the nitrided layer, 11 mu m The coating hardness and Young's Modulus were about 16 and 110 GPa, respectively. The duplex samples resulted with better adhesion than the only coated samples in all test conditions. In the scratch test, the critical load in the duplex sample was 58 N and in the coated sample, 12 N, showing a brittle failure mode. In the Rockwell C indentation test, the adhesion was better in the duplex sample because the nitriding treatment changed the failure mode of the system. The wear resistance was also related to adhesion, since in the experiments with high loads and long durations adhesive failures could be detected when stresses reached the interface and the substrate. In the duplex sample, the nitrided case, with higher load bearing capacity than the substrate, resulted in a better wear behavior of the system. |
Área | FISMAT |
Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Fretting wear resistance... |
Conteúdo da Pasta doc | acessar |
Conteúdo da Pasta source | não têm arquivos |
Conteúdo da Pasta agreement | |
|
4. Condições de acesso e uso | |
Idioma | en |
Arquivo Alvo | 1-s2.0-S223878541730265X-main.pdf |
Grupo de Usuários | simone |
Grupo de Leitores | administrator simone |
Visibilidade | shown |
Permissão de Leitura | deny from all and allow from 150.163 |
Permissão de Atualização | não transferida |
|
5. Fontes relacionadas | |
Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 |
Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.24.19.30 5 |
Divulgação | PORTALCAPES; SCOPUS. |
Acervo Hospedeiro | urlib.net/www/2017/11.22.19.04 |
|
6. Notas | |
Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project resumeid rightsholder schedulinginformation secondarydate secondarykey secondarymark session shorttitle sponsor subject tertiarymark tertiarytype url |
|
7. Controle da descrição | |
e-Mail (login) | simone |
atualizar | |
|